Study Structure and Properties of Reinforcing Rolled Coils by V-Alloyed C – Mn – Si - Steel with Dual- and Multi-Phase Microstructures


  •  V. L. Plyuta    
  •  S. A. Vorobey    
  •  G. V. Levchenko    
  •  A. B. Sychkov    
  •  A. M. Nesterenko    

Abstract

Thermo-mechanical controlled rolling (TMCR) schedules have been studied on the wire line of 400/200 section rolling mill to manufacture 6.0 – mm - diameter reinforcing wire in coils by V-alloyed C – Mn – Si - steel that has dual-phase (DP - ferrite-martensite (bainite)) and multi-phase (MP - ferrite-martensite (bainite) - pearlite) microstructures.

It has been established that high tensile strength and plasticity values were achieved in this 6.0 – mm wire in coils (YS0.2= 530-550 MPa; TS= 785 – 885 MPa; El= 15.0 – 29.0 %) which were in full compliance with national standard specifications such as ASТM A 615 (USA), JIS G 3112 (Japan) and KSD 3504 (the Republic of Korea)), when the TMCR schedules involving laying head temperatures ТLH from 1024 ºС to 1063 ºС were employed ensuring formation of MP microstructure.



This work is licensed under a Creative Commons Attribution 4.0 License.
  • ISSN(Print): 1927-0585
  • ISSN(Online): 1927-0593
  • Started: 2012
  • Frequency: quarterly

Journal Metrics

Google-based Impact Factor (2017): 5.94
h-index (January 2018): 13
i10-index (January 2018): 20
h5-index (January 2018): 12
h5-median (January 2018): 26

Learn more

Contact