Study on Preparation and Property of CaCO3-filled SF/PVA Blend Films
- Wei Wang
- Lu Qi
Abstract
In order to solve the problems of the poor binding capacity, forming the aggregate easily between the surface of calciumcarbonate powder and SF/PVA blend system, causing the dispersion inhomogeneous in the organic blending system.
The CaCO3-filled SF/PVA blend films were prepared by blending solution with CaCO3 treated with titanate coupling
agent. According to IR, the introduction of titanate coupling agent was indeed to crosslink the CaCO3 with PVA and SF.
DSC showed that the compatibility of each component of blend films had obviously changed by adding of glycerin.
When the content of calcium carbonate was 5wt%, the improving of the tensile strength, elongation at break mechanical
properties and the stability of wet of blend films had obvious effect. In addition, when the content of titanate coupling
agent was 0.3wt%, the blend films exhibited a breaking strength of 45.26Mpa and 832.78% elongation at break,
dissolve-loss rates were 2.88%. After the content of titanate coupling agent increased, the mechanical properties
decreased and dissolve-loss rates increased gradually.
- Full Text: PDF
- DOI:10.5539/ijc.v2n1p174
This work is licensed under a Creative Commons Attribution 4.0 License.
Journal Metrics
h-index (December 2022): 32
i10-index (December 2022): 145
h5-index (December 2022): N/A
h5-median(December 2022): N/A
( The data was calculated based on Google Scholar Citations. Click Here to Learn More. )
Index
- Academic Journals Database
- Bibliography and Index of Geology
- CAB Abstracts
- CAS (American Chemical Society)
- COPAC
- Elektronische Zeitschriftenbibliothek (EZB)
- EuroPub Database
- Excellence in Research for Australia (ERA)
- Genamics JournalSeek
- Google Scholar
- Infotrieve
- Mendeley
- MIAR
- RePEc
- ResearchGate
- ROAD
- SHERPA/RoMEO
Contact
- Albert JohnEditorial Assistant
- ijc@ccsenet.org