Investigation on Preparation and Porosity of YSZ/PTFE Microporous Membrane Modified by PTFE Resin Emulsion
- Jinli Du
- Xinhua Deng
- Yuan Sun
Abstract
In this paper, YSZ/PTFE composite microporous membrane was prepared by mechanical tensile method, using PTFE resin emulsion as material and YSZ micro/nanoparticles as reinforcer. The performance of YSZ/PTFE composite microporous membrane was characterized by mechanical property testing. The effects of the dispersant PVA, the draw ratio, YSZ content and calcination temperature on the porosity of composite microporous membrane were systematically investigated. The results showed that the porosity increased significantly as PVA added; with the increase of YSZ content, the porosity gradually increased, but the YSZ content was not over 20%; the porosity reached 73.09% when the draw ratio 3.5 times, YSZ content 8%, and the calcination temperature 320?.
- Full Text: PDF
- DOI:10.5539/mas.v4n11p78
Journal Metrics
(The data was calculated based on Google Scholar Citations)
h5-index (July 2022): N/A
h5-median(July 2022): N/A
Index
- Aerospace Database
- American International Standards Institute (AISI)
- BASE (Bielefeld Academic Search Engine)
- CAB Abstracts
- CiteFactor
- CNKI Scholar
- Elektronische Zeitschriftenbibliothek (EZB)
- Excellence in Research for Australia (ERA)
- JournalGuide
- JournalSeek
- LOCKSS
- MIAR
- NewJour
- Norwegian Centre for Research Data (NSD)
- Open J-Gate
- Polska Bibliografia Naukowa
- ResearchGate
- SHERPA/RoMEO
- Standard Periodical Directory
- Ulrich's
- Universe Digital Library
- WorldCat
- ZbMATH
Contact
- Sunny LeeEditorial Assistant
- mas@ccsenet.org