Preparation of LaFeO3 Porous Hollow Nanofibers by Electrospinning


  •  Xiangting Dong    
  •  Jinxian Wang    
  •  Qizheng Cui    
  •  Guixia Liu    
  •  Wensheng Yu    

Abstract

Polyvinyl Pyrrolidone (PVP)/[La(NO3)3+Fe(NO3)3] composite nanofibers were fabricated by electrospinning. SEM
micrographs indicated that the surface of the prepared composite fibers was smooth, and the diameters of the nanofibers
was in the range of 1-3μm. XRD analysis revealed that the composite nanofibers were amorphous in structure. LaFeO3
nanofibers were fabricated by calcination of the PVP/[La(NO3)3+Fe(NO3)3] composite fibers. The diameters of LaFeO3
nanofibers were smaller than those of the relevant composite fibers. The surface of the LaFeO3 nanofibers became
coarse with the increase of calcination temperatures. LaFeO3 hollow-centered and porous nanofibers formed by
nanoparticles were acquired when firing temperature was 600-800ºC. SEM images indicated that the diameters of the
synthesized LaFeO3 nanofibers ranged from 500 to 800nm, and their lengths were greater than 100????m. XRD analysis
revealed that LaFeO3 nanofibers were orthorhombic in structure with space group Pn*a. Possible formation mechanism
for LaFeO3 nanofibers was preliminarily proposed.


This work is licensed under a Creative Commons Attribution 4.0 License.
  • ISSN(Print): 1916-9698
  • ISSN(Online): 1916-9701
  • Started: 2009
  • Frequency: semiannual

Journal Metrics

h-index (December 2022): 32

i10-index (December 2022): 145

h5-index (December 2022): N/A

h5-median(December 2022): N/A

( The data was calculated based on Google Scholar Citations. Click Here to Learn More. )

Contact